G10 Insulating iav Epoxy Laminate
Cov tuab tuab: 0.5 ~ 100mm
Qhov loj me: 1020 × 2040mm
Electronic qib alkali-dawb iav fiber ntau daim ntaub yog impregnated nrog imported epoxy resin, thiab ntxiv nrog coj txawv txawv nplaim retardants, adhesives thiab lwm yam additives, thiab ua tiav los ntawm kub nias.nplaim retardant qib UL94-VO qib, zoo txhua yam khoom ntawm qhov kub thiab txias, kev ua haujlwm zoo thiab kev ua haujlwm rwb thaiv tsev.
G10 epoxy board daim ntawv thov: siv los ua cov khoom siv hluav taws xob hauv cov khoom siv hluav taws xob thiab cov khoom siv hluav taws xob, xws li cov khoom siv hluav taws xob, cov khoom siv hluav taws xob, cov hloov pauv, DC motors, AC contactors, cov khoom siv hluav taws xob tawg thiab lwm yam khoom siv hluav taws xob.
Tsis muaj. | Cov khoom | Chav tsev | Txheem tus nqi | Cov txiaj ntsig kuaj |
1 | Flexural zog perpendicular rau laminations | MPa | GB/T1303.4-2009 | ≥340 |
2 | Khoov elastic modulus | MPa | GB/T1303.4-2009 | / |
3 | Notch Impact lub zog sib npaug rau lamination (charpy) | kJ/m2 | GB/T1303.4-2009 | ≥33 |
4 | Tensile zog | MPa | GB/T1303.4-2009 | / |
5 | Dielectric zog perpendicular rau laminations (hauv roj 20±2℃) | KV/mm | GB/T1303.4-2009 | ≥11.4 |
6 | Breakdown voltageparallel rau lamination (hauv vaj90±2℃) | KV | GB/T1303.4-2009 | ≥35 |
7 | 1 MHz poob yam | / | GB/T1303.4-2009 | / |
8 | Rwb thaiv tsev tiv thaiv impregnated hauv dej | MΩ | GB/T1303.4-2009 | ≥5 x 10 000 |
9 | CTI | / | GB/T 4207-2012 | / |
10 | Kev nqus dej | mg | GB/T 1303.4-2009 | ≤27 |
11 | Qhov ntom | g/cm3 | GB/T 1303.4-2009 | / |